Welding Electrode
Carbon Steel Electrode
Carbon steel welding electrode( E6013) is suitable to work in all positions with excellent welding technological properties, stable arc less splash, shaped good appearance, easy for removal of slag layer, easy for striking arc and restriking arc.
Used for welding common carbon steel structure, suitable for small thin plates and low class low-allow steel. Such as 09Mn2.
Advantages:
Model |
GB |
AWS |
Chemical Composition |
Mechanical Test |
|||||||
C |
Mn |
Si |
S |
P |
Rm(MPa) |
ReL(Mpa) |
A(%) |
KV2(J) |
|||
SQ.J421 |
E4313 |
E6013 |
≤0.12 |
0.3~0.6 |
≤0.35 |
≤0.035 |
≤0.040 |
≥420 |
≥330 |
≥17 |
|
SQ.J421Fe16 |
E4324 |
E6024 |
≤0.12 |
0.30~0.60 |
≤0.35 |
≤0.035 |
≤0.040 |
≥420 |
≥330 |
≥17 |
|
SQ.J421Fe18 |
E4324 |
E6024 |
≤0.12 |
0.30~0.60 |
≤0.35 |
≤0.035 |
≤0.040 |
≥420 |
≥330 |
≥17 |
|
SQ.J422 |
E4303 |
|
≤0.12 |
0.3~0.6 |
≤0.25 |
≤0.035 |
≤0.040 |
≥420 |
≥330 |
≥22 |
≥27(0℃) |
SQ.J501Fe18 |
E4024 |
E7024 |
≤0.12 |
≤1. 25 |
≤0.90 |
≤0.035 |
≤0.040 |
≥490 |
≥400 |
≥17 |
≥27(0℃) |
SQ.J502 |
E5003 |
|
≤0.12 |
≤1.60 |
≤0.3 |
≤0.035 |
≤0.040 |
≥490 |
≥400 |
≥20 |
≥27(0℃) |
SQ.J506 |
E5016 |
E7016 |
≤0.12 |
≤1.60 |
≤0.75 |
≤0.035 |
≤0.040 |
≥490 |
≥400 |
≥22 |
≥47(-20℃) |
SQ.J506Fe |
E5018 |
E7018 |
≤0.12 |
≤1.60 |
≤0.75 |
≤0.035 |
≤0.040 |
≥490 |
≥400 |
≥22 |
≥27(-30℃) |
SQ.J506Fe-1 |
E5018-1 |
E7018-1 |
≤0.12 |
≤1.60 |
≤0.75 |
≤0.035 |
≤0.035 |
≥490 |
≥400 |
≥23 |
≥47(-40℃) |
SQ.J507 |
E5015 |
E7015 |
≤0.12 |
≤1.60 |
≤0.75 |
≤0.035 |
≤0.040 |
≥490 |
≥400 |
≥22 |
≥47(-20℃) |
SQ.J507Fe |
E5018 |
E7018 |
≤0.12 |
≤1.60 |
≤0.75 |
≤0.035 |
≤0.040 |
≥490 |
≥400 |
≥22 |
≥27(-30℃) |
SQ.J507Fe16 |
E5028 |
E7028 |
≤0.12 |
≤1.60 |
≤0.75 |
≤0.035 |
≤0.040 |
≥490 |
≥400 |
≥22 |
≥27(-20℃) |
Pipe Welding Electrode
Model |
GB |
AWS |
Chemical Composition |
Mechanical Test |
|||||||
C |
Mn |
Si |
S |
P |
Cr |
Rm(MPa) |
ReL/Rp0.2(Mpa) |
A(%) |
|||
SQ.E6010 |
E4310 |
E6010 |
≤0.20 |
0.3~0.6 |
≤0.2 |
≤0.035 |
≤0.040 |
~0.30 |
≥450 |
≥340 |
22~28 |
SQ.E6010 |
E4311 |
E6011 |
≤0.20 |
0.3~0.6 |
≤0.2 |
≤0.035 |
≤0.040 |
~0.30 |
≥450 |
≥340 |
22~28 |
Surfacing Electrode
Model |
GB |
AWS |
Chemical Composition |
Hardness |
|||
SQ.D707 |
|
|
C |
Mn |
Si |
W |
HRC≥60 |
1.50~3.00 |
≤2.00 |
≤4.00 |
40.0~50.0 |
||||
SQ.D256 |
EDMn-A-16 |
EFeMn-A |
C |
Mn |
Si |
|
HB≥170 |
≤1.10 |
11.0~16.0 |
≤1.30 |
|
||||
SQ.D217A |
EDPCrMo-A3-15 |
|
C |
Mo |
Cr |
|
HRC≥40 |
≤0.50 |
≤2.50 |
≤2.50 |
|
Cast iron welding electrode with excellent crack resistance and process-ability, can work with AC or DC power, stable arc, electrode without becoming red, easy for operating.
Suitable for repair welding on thin cast iron pieces and machined surfaces, such as some key gray cast iron pieces like engine bearers, guide rails of machine tools, pinion stands, etc.
Model |
GB |
AWS |
Chemical Composition |
|||||||
C |
Mn |
Si |
S |
Cu |
Ni |
Fe |
Other Elements |
|||
SQ.Z208 |
EZC |
EC1 |
≤2.00 |
≤1.00 |
≤2.50 |
≤0.030 |
|
≥90 |
≤8 |
≤1.00 |
SQ.Z308 |
EZNi-1 |
ENi-C1 |
≤2.00 |
≤1.00 |
|